标題: Excellent low temperature NH3-SCR and NH3-SCO performance over Ag-Mn/Ce-Ti catalyst: Evaluation and characterization

作者: Liu, WJ (Liu, Wenjie); Long, YF (Long, Yifei); Zhou, YY (Zhou, Yongyan); Liu, SN (Liu, Shinian); Tong, X (Tong, Xin); Yin, YJ (Yin, Yajie); Li, XY (Li, Xiaoyi); Hu, K (Hu, Kang); Hu, JJ (Hu, Jiangjun)

來源出版物: MOLECULAR CATALYSIS 卷: 528 文獻号: 112510 DOI: 10.1016/j.mcat.2022.112510 出版年: AUG 2022

摘要: Low temperature SCR has been a promising technology due to the diverse load in coal-fired plants. However, ammonia escape problem could be more serious at low temperature on account of the condensation of NH4HSO4, resulting in deactivation of SCR catalyst and equipment corrosion. NH3-SCO technology could oxidize slip ammonia to harmless N-2. Hence, it is important to develop a novel catalyst with high SCR and SCO efficiency at low temperature to remove NOx and slip NH3 and achieve the stable operation of SCR system. In this work, a combined sol-gel and impregnation method was used to synthetize different Aga_Mn/Ce-Ti (a = 2%, 5%, 8%) catalysts and applied in NOx and slip NH3 removal at low temperature. The activity measurement confirmed that Ag-5-Mn/Ce-Ti catalyst exhibited an excellent low-temperature performance. At 150-300 C, its NO conversion was 100%, NH3 conversion was above 95% and N-2 selectivity was more than 90%. Moreover, considering the oxidation of slip ammonia, Ag-5-Mn/Ce-Ti catalyst also exhibited above 90% NH3 conversion at 200-350 C in the absence of NO. The catalytic performance could also be kept at a high level under the existence of SO2 and H2O. The characteristic results revealed that Ag and Mn modification could not apparently change the phase structure and could decrease the BET area to some extent. In addition, Ag-Mn/Ce-Ti catalyst possessed stronger and more surface acidic sites and contributed to better NH3 adsorption capacity. Besides, there was more chemisorbed oxygen on Ag-Mn/Ce-Ti catalyst resulting from the interactions among Ag, Mn and Ce oxides, which was responsible for its better redox property.

文獻類型: Article

作者關鍵詞: Ag modification; Ce-Ti catalyst; Low-temperature SCR; Slip ammonia

地址: [Liu, Wenjie; Long, Yifei; Tong, Xin; Yin, Yajie; Li, Xiaoyi; Hu, Kang; Hu, Jiangjun] Wuhan Univ, School Resource & Environm Sci, Wuhan 430079, Hubei, Peoples R China.

[Zhou, Yongyan] Electric Power Res Inst Guangdong Power Grid Co. L, Guangzhou, Peoples R China.

[Liu, Shinian] China Southern Power Grid Technology Co Ltd, Guangzhou 510080, Peoples R China.

通訊作者地址: Hu, JJ (通訊作者)，Wuhan Univ, School Resource & Environm Sci, Wuhan 430079, Hubei, Peoples R China.

電子郵件地址: jjhu1963@outlook.com

影響因子：5.089