标題：Plasma Modification of Activated Carbon Fibers for Adsorption of SO2作者：Che Yao; Zhou Jiayong; Wang Zuwu

來源出版物：PLASMA SCIENCE & TECHNOLOGY 卷：15 期：10 頁：1047-1052;

DOI：10.1088/1009-0630/15/10/16 出版年：OCT 2013

摘要：Viscose-based activated carbon fibers (VACFs) were treated by a dielectric-barrier discharge plasma under the feed gas of N-2. The surface functional groups of VACFs were modified to improve the adsorption and catalysis capacity for SO2. The surface properties of the untreated and plasma-treated VACFs were diagnosed by SEM, BET, FTIR, and XPS, and the adsorption capacities of VACFs for SO2 were also compared and discussed. The results show that after the plasma treatment, the external surface of VACFs was etched and became rougher, while the surface area and the total pore volume decreased. FTIR and XPS revealed that nitrogen atoms were introduced onto the VACFs surface and the distribution of functional groups on the VACFs surface was changed remarkably. The adsorption characteristic of SO2 indicates that the plasma-treated VACFs have better adsorption capacity than the original VACFs due to the nitrogen functional groups and new functional groups formed in modification, which is beneficial to the adsorption of SO2.

入藏号：WOS:000326147400016

文獻類型：Article

語種：English

作者關鍵詞：cold plasma, surface modification, activated carbon fibers, adsorption, SO2

擴展關鍵詞：SULFUR-DIOXIDE; AMMONIA; REMOVAL; ENHANCEMENT; COMPOSITES; ACID; AIR

通訊作者地址：Che Yao; Wuhan Univ, Coll Resource & Environm Sci, Wuhan 430079, Peoples R China.

電子郵件地址：cheyao@whu.edu.cn

地址：

[Che Yao; Zhou Jiayong; Wang Zuwu] Wuhan Univ, Coll Resource & Environm Sci, Wuhan 430079, Peoples R China.

研究方向：Physics

ISSN：1009-0630