标題:Coating titanium on carbon steel by in-situ electrochemical reduction of solid TiO2 layer

作者:Xiao, ZA (Xiao, Zuo-an); Tang, DY (Tang, Di-yong); Fan, JH (Fan, Jin-hang); Xiao, W (Xiao, Wei); Wang, DH (Wang, Di-hua)

來源出版物:TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA 卷:27 期:1 頁碼:134-140 DOI: 10.1016/S1003-6326(17)60015-3 出版年: JAN 2017

摘要:Ti coating on A3 steel was successfully prepared by direct electrochemical reduction of high-velocity oxy-fuel (HVOF) thermally sprayed and room-temperature dip-coating titanium dioxide coating on A3 steel in molten CaCl2 at 850 degrees C. The interfacial microstructure and mutual diffusion between coating and steel substrate were investigated using scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy. The results show that the precursory TiO2 coating prepared by HVOF has closer contact and better adhesion with the A3 steel substrate. After electrolysis, all of the electro-generated Ti coatings show intact contact with the substrates, regardless of the original contact situation between TiO2 layer and the steel substrate in the precursors. The inter-diffusion between the iron substrate and the reduced titanium takes place at the interface. The results demonstrate the possibility of the surface electrochemical metallurgy (SECM) is a promising surface engineering and additive manufacturing method.

入藏号: WOS:000394413200015

文獻類型:Article

語種:English

作者關鍵詞: Ti coating; molten salt; surface metallurgy; electrochemical reduction; additive manufacturing

擴展關鍵詞:MOLTEN CALCIUM-CHLORIDE; ELECTRO-DEOXIDATION; OXIDE; CORROSION; POWDERS; ALLOY; METAL; ELECTROREDUCTION; PRECURSORS; DIOXIDE

通訊作者地址:Wang, DH (reprint author), Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

電子郵件地址:wangdh@whu.edu.cn

地址: [Xiao, Zuo-an; Tang, Di-yong; Fan, Jin-hang; Xiao, Wei; Wang, Di-hua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

研究方向:Metallurgy & Metallurgical Engineering

ISSN:1003-6326

eISSN:2210-3384

影響因子:1.34

信息服務
學院網站教師登錄 學院辦公電話 學校信息門戶登錄

版權所有 © 88858cc永利官网
地址:湖北省武漢市珞喻路129号 郵編:430079 
電話:027-68778381,68778284,68778296 傳真:027-68778893    郵箱:sres@whu.edu.cn

Baidu
sogou