博士生範金航的論文在JOURNAL OF THE ELECTROCHEMICAL SOCIETY 刊出
發布時間:2017-09-01 15:35:29     發布者:yz     浏覽次數:

标題:Electrochemical Synthesis of Nano-Metallic Carbides from the Mixtures of Metal Oxide and Graphite

作者:Fan, JH (Fan, Jinhang); Yang, YJ (Yang, Yijia); Tang, DD (Tang, Dingding); Xiao, W (Xiao, Wei); Mao, XH (Mao, Xuhui); Wang, DH (Wang, Dihua)

來源出版物:JOURNAL OF THE ELECTROCHEMICAL SOCIETY 卷:164 期:7 頁碼:E144-E150 DOI:10.1149/2.0471707jes 出版年:2017

摘要:Nanocrystalline transition metal carbides (TMCs, M = Ti, Zr, Hf, Nb and Ta) have been synthesized by direct electrochemical reduction of solid mixture precursors composed of transition metal oxides and graphite powder (TMOs-C) in molten CaCl2 at 850 degrees C. The synthesis temperature is much lower than that of the conventional carbothermic reduction process. SEM analysis showed that the particle sizes of the as-prepared TMCs powders were about 15-30 nm. The formation processes of nanocrystalline TMCs monitored by analyzing partially reduced samples were confirmed to be similar to each other and could be divided into three steps: TMOs-C first to CaMaOb and MCxOy, then to pure MCxOy and last to MC. It has been found that the electrolysis production of (TMCs)-Cs-V is much faster than that of (TMCs)-Cs-IV. The formation of intermediate MCxOy during the electrolysis processes was investigated and their stability should be the key influence factor of the electro-deoxidation rate of the mixtures. (C) 2017 The Electrochemical Society.

入藏号:WOS:000404397300108

文獻類型:Article

語種:English

擴展關鍵詞: CHEMICAL-VAPOR-DEPOSITION; MOLTEN CALCIUM-CHLORIDE; NANOCRYSTALLINE TITANIUM CARBIDE; NIOBIUM CARBIDE; LOW-TEMPERATURE; CARBOTHERMAL SYNTHESIS; TIC POWDERS; SOLID NB2O5; REDUCTION; PRECURSORS

通訊作者地址:Wang, DH (通訊作者),Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

電子郵件地址:wangdh@whu.edu.cn

地址: [Fan, Jinhang; Yang, Yijia; Tang, Dingding; Xiao, Wei; Mao, Xuhui; Wang, Dihua] Wuhan Univ, Sch Resource & Environm Sci, Wuhan 430072, Peoples R China.

研究方向:Electrochemistry; Materials Science

ISSN:0013-4651

eISSN: 1945-7111

影響因子:3.259

信息服務
學院網站教師登錄 學院辦公電話 學校信息門戶登錄

版權所有 © 88858cc永利官网
地址:湖北省武漢市珞喻路129号 郵編:430079 
電話:027-68778381,68778284,68778296 傳真:027-68778893    郵箱:sres@whu.edu.cn

Baidu
sogou